Polyaniline nanofibers; Electrode material; Supercapacitor; Aqueous dispersion
资金
- National Science Foundation of China [51073156, 51021003]
Aqueous dispersed conducting polyaniline nanofiber, new electrode material for supercapacitor, is prepared employing acidic phosphate ester as dopant for nanofibrous polyaniline emeraldine base, which is synthesized by polymerization of aniline using ferric nitrate as oxidant through pseudo-high dilution technique. Highly crystalline and uniform polyaniline fibers with thin diameter of 17-26 nm are obtained, the film from which shows electrical conductivity of 32 S cm(-1). The thin nanofibrous polyaniline is used as electrode material for supercapacitor and its performance is evaluated in non-protonic solvent system. It shows a specific capacitance as high as 160 F g(-1) at discharge rate of 0.4 A g(-1) from -1V to 1 V in 1 mol L-1 tetraethylammonium tetrafluoroborate/propylene carbonate solution, and the discharge/charge efficiency reaches 92%, indicating that it possesses good electrochemical reversibility. The high capacitance can be attributed to its relatively high surface area of 70 m(2) g(-1), which is 3-5 times higher than spherical polyaniline or thick fiberous polyaniline, leading to high utilization of the electroactive materials. (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据