Fuel cell; Composite membrane; Open circuit voltage degradation; Relative humidity cycling; Load cycling
资金
- National Science Council of Taiwan [NSC 98-2622-E-155-074-CC3, NSC 98-3114-E-155-001]
The main purpose of this study is to investigate the accelerated degradation of the PTFE/Nafion membrane electrode assembly through open circuit voltage and relative humidity cycling The state of a PTFE/Nafion membrane electrode assembly is evaluated in a fuel cell by monitoring the polarization curve AC impedance cyclic voltammetry and linear sweep voltammetry data over time The experimental results are then fitted to equations of an equivalent circuit The results of the first 160 experimental cycles show that catalyst degradation is the main cause for the decay of the membrane electrode assembly During the 160-520th cycles the membrane electrode assembly experiences creep deformation which is due to relative humidity cycling During the 640-840th cycles the degradation causes a gradual transition from minor to major membrane cracking after which the combustion reaction dramatically accelerates membrane electrode assembly degradation (C) 2010 Elsevier B V All rights reserved
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据