Li-ion battery; Cathode material; Li[Ni0.17Li0.2Co0.07Mn0.56]O-2; Pre-cycling treatment; Cyclic deterioration; TEM
资金
- Japanese New Energy and Industrial Technology Development Organization (NEDO)
Transmission electron microscopy (TEM) studies were carried out to elucidate cyclic deterioration phenomena for Li-rich layered cathode material Li[Ni0.17Li0.2Co0.07Mn0.56]O-2. The results obtained show that the deterioration starts during the initial charge/discharge to higher potential over 4.5 V, and leads to the formation of micro-cracks at the crystal surface and the distortion of crystal periodicity. These two kinds of defects lead to further non-crystallization of the crystal surface and the emergence of a very small amount of another possible phase. Our stepwise pre-cycling treatment effectively depressed the formation of the former two kinds of defects, and could significantly improve cyclic durability. The observation of non-crystallization at the cathode crystal surface, which would diminish the battery performance, is consistent with our preliminary ac impedance results. (C) 2009 Elsevier B. V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据