期刊
JOURNAL OF POWER SOURCES
卷 195, 期 16, 页码 5185-5196出版社
ELSEVIER
DOI: 10.1016/j.jpowsour.2010.02.079
关键词
LSCF; Solid oxide fuel cell; Cathode; Thin film; Microstructure; Stress
资金
- SiEnergy Systems
- National Science Foundation
- Harvard SEAS
- Direct For Computer & Info Scie & Enginr
- Div Of Information & Intelligent Systems [0926148] Funding Source: National Science Foundation
Microstructure and stresses in dense La0.6Sr0.4Co0.8Fe0.2O3 (LSCF) ultra-thin films have been investigated to increase the physical thickness of crack-free cathodes and active area of thermo-mechanically robust micro-solid oxide fuel cell (mu SOFC) membranes. Processing protocols employ low deposition rates to create a highly granular nanocrystalline microstructure in LSCF thin films and high substrate temperatures to produce linear temperature-dependent stress evolution that is dominated by compressive stresses in mu SOFC membranes. Insight and trade-off on the synthesis are revealed by probing microstructure evolution and electrical conductivity in LSCF thin films, in addition to in situ monitoring of membrane deformation while measuring mu SOFC performance at varying temperatures. From these studies, we were able to successfully fabricate failure-resistant square mu SOFC (LSCF/YSZ/Pt) membranes with width of 250 mu m and crack-free cathodes with thickness of similar to 70 nm. Peak power density of similar to 120 mW cm(-2) and open circuit voltage of similar to 0.6V at 560 degrees C were achieved on a mu SOFC array chip containing ten such membranes. Mechanisms affecting fuel cell performance are discussed. Our results provide fundamental insight to pathways of microstructure and stress engineering of ultra-thin, dense oxide cathodes and mu SOFC membranes. (C) 2010 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据