The waterborne polyurethane (PU) prepolymer was prepared based on isophorone diisocyanate (IPDI), polyester polyol (N220), dimethylol propionic acid (DMPA) and hydroxyethyl methyl acrylate (HEMA). The modified waterborne polyurethane-acrylate (PUA) emulsions were obtained with different proportions of acrylate (butyl acrylate and methyl methacrylate) and initiating agent by in situ dispersion technique. The structures and thermal properties of prepared PU and PUA were analyzed and characterized with FT-IR, UV-Vis spectroscopy and DSC. The PUA hybrid samples had lower glass transition temperature of hard segment and higher decomposition temperatures than PU sample. Performances of the emulsion and film were studied by means of apparent viscidity, particle size and polydispersity, surface tension and mechanical properties. The results indicated that the particle sizes of the PUA dispersions were larger than those of the pure PU and the solvent resistance, mechanical properties of PUA films was improved compare with the unmodified polyurethane film. The film had the biggest hardness and the least water absorption when the BA/MMA mass ratio 5:5 modified PU. The obtained PUA have great potential application such as coatings, leather finishing, adhesives, sealants, plastic coatings and wood finishes.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据