coatings; core-shell polymers; glycidyl methacrylate; magnetic polymers; methacrylate phosphate; nanoparticles; particle size distribution
资金
- Grant Agency of the Academy of Sciences of the Czech Republic [KAN401220801]
- Grant Agency of the Czech Republic [203/09/1242, 203/09/0857]
Maghemite (gamma-Fe2O3) colloid has been synthesized by coprecipitation of ferrous and ferric salts in alkaline medium and oxidation. The obtained nanoparticles were complexed with a phosphate macromonomer-penta(propylene glycol) methacrylate phosphate (PPGMAP). Complexes with the weight ratio PPGMAP/gamma-Fe2O3 0.01-10 were investigated using a range of characterization methods. The amount of PPGMAP attached to the particles was about 22 wt %. The size and size distribution of the gamma-Fe2O3 core particles in the dry state was measured by TEM. To complete the TEM images, the hydrodynamic size of the nanoparticles including polymer shell and the maghemite core was determined by DLS measurements in toluene. Magnetic poly(glycidyl methacrylate) (PGMA) nanospheres were obtained by Kraton G 1650-stabilized and 2,2'-azobisisobutyronitrile-initiated polymerization of glycidyl methacrylate (GMA) in toluene or toluene/cyclohexane mixture in the presence of PPGMAP-coated gamma-Fe2O3 colloid. The effect of Kraton G 1650 concentration on the morphology, PGMA nanosphere size and polydispersity was investigated. The particles were characterized also by both thermogravimetric analysis and magnetic measurements. (C) 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 4982-4994, 2009
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据