Non-isocyanate route; Thermoplastic; Poly(amide urethane)s; Polycondensation; Diurethanediol; Transurethanization
资金
- National Natural Science Foundation of China [21244006, 50873013]
Two nylon-6 oligomers having polymerization degrees of 4.99 and 3.55 terminated with H2N- and HO- groups (H2N-PA-OHs) were prepared by the ring-opening polymerization of caprolactam with ethanolamine at different molar ratios. These oligomers were transformed into HO-terminated nylon-6 oligomers (HO-PA-OHs) through reaction with excessive caprolactone. The transurethane polycondensation of HO-PA-OHs with a diurethanediol, i.e., 1,6-bis(hydroxyethyloxy carbonyl amino)hexane (BHCH), was carried out at 170 A degrees C under normal pressure for 4 h and at 180 A degrees C under a reduced pressure of 3 mmHg for 6.5 h. A series of aliphatic thermoplastic poly(amide urethane)s having different short nylon-6 segments (s-PAUs) was prepared. The s-PAUs were characterized by viscometry, gel permeation chromatography, FT-IR, H-1-NMR, solid C-13 CP MAS NMR, differential scanning calorimetry, thermogravimetric analysis, wide angle X-ray scattering and tensile tests. Results showed Mn above 29,762, Mw above 36,725, Tm between 128.73 and 171.69 A degrees C, and initial decomposition temperature over 266.25 A degrees C. Tensile strength reached 31.50 MPa with strain at break up to 447.49 %. Some urea linkages were formed during transurethane polycondensation.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据