JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS
卷 73, 期 8, 页码 1040-1043出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.jpcs.2012.03.009
关键词
Nanostructures; Sol-gel growth; Crystal structure; Electrical properties
Lithium doped cobalt ferrites (Li0.2CoFe1.8O4) were prepared by a sol-gel combustion method by using Lithium nitrate, cobalt nitrate, and ferric nitrate as source materials. Here, Citric acid and polyvinyl alcohol used as a burning agent and agglomeration reducing agent respectively. The pH value of precursor was maintained between 7 and 8 while preparation of the sample. The average particle size of the ferrite obtained at 300 degrees C about similar to 15-20 nm. Further, single phase spinel structure has been confirmed by X-ray diffraction (XRD) and Cubic morphology was confirmed by High resolution scanning electron microscopy (HR-SEM). The composition of elements has been confirmed by Infrared spectroscopy (FT-IR). Moreover, the electrical studies of the prepared sample have been analyzed by four point probe method. The observed results inferred that conductivity of the ferrite sample has been reduced by addition of lithium. (C) 2012 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据