Octacalcium phosphate (OCP) powder was produced by precipitating 250 mL Ca(CH3COO)(2) 0.04 M into 750 L of phosphate solution (5 mmol Na2HPO4 and 5 mmol NaH2PO4) at a constant temperature of 60 degrees C and pH 5, which resulted in a dry white powder. X-ray diffraction (XRD), transmission electron microscopy (TEM) analysis, and the electron diffraction pattern (SAED) all showed only OCP. Hydroxyapatite (HAP) was directly obtained through hydrolysis of the powder. The total transformation of OCP into HAP was registered over a period of 6 h. During the first 30 min of hydrolysis both phases coexisted. The two phases and the OCP-HAP interface were structurally analyzed through XRD and TEM. OCP parameters (calculated by the Rietveld method) are a = 19.70, b = 9.50, c = 6.85 angstrom; alpha = 90.03 degrees, beta = 92.48 degrees, gamma = 108.32 degrees (triclinic P-1) with average crystal size of 13.5+/-0.2 nm, while HAP parameters were a = 9.45, c = 6.87 angstrom (hexagonal P6(3)/M) with average crystal size of 16.9+/-0.2 nm. (C) 2008 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据