关键词
Magnetic materials; Metals; Electron microscopy; Microstructure
资金
- University Research Talents [2005KYCX021]
A facile hydrothermal reduction route based on a precipitate slow-release controlled process was developed to fabricate highly ordered dendritic cobalt microcrystals using cetyltrimethylammonium bromide (CTAB) in high alkali media. The shape, structure, and magnetic properties of the final products were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), transmission electron microscopy (TEM), electron diffraction (ED), and vibrating sample magnetometry (VSM). The results showed that the sample is hexagonal close-packed Co coexisting with cubic close-packed Co: the length of the main trunk is about 8 pm and diameter of the branches is 0.5-2 mu m. Magnetic measurement at 300 K showed that these In microstructures exhibited ferromagnetic character. The probable formation mechanism of the microcrystals was discussed on the basis of the experimental results. (C) 2008 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据