JOURNAL OF PHYSICAL CHEMISTRY C
卷 114, 期 2, 页码 922-928出版社
AMER CHEMICAL SOC
DOI: 10.1021/jp9097606
关键词
-
资金
- Research Council of Norway [163565/431, 158518/431]
- NanoEnvironment project
Mn5O8 nanorods were prepared by a topotactic conversion of gamma-MnOOH nanorod precursors in nitrogen at 400 degrees C. The as-prepared Mn5O8 nanorods crystallized in a monoclinic structure (space group C2/m) with unit cell dimensions a = 10.3784(2) angstrom, b = 5.7337(7) angstrom, c = 4.8668(6) angstrom, and beta = 109.491(6)degrees, having a compositional formula Mn22+Mn34+O8. The structure allowed 18 Raman-active modes (10 A(g) + 8 B-g); 10 of these contributions were observed at 262, 300, 391, 429, 475, 533, 576, 615, 647, and 789 cm(-1). An intensive A(g) mode at 647 cm(-1) was identified, representing a clear signature for probing the Mn5O8 materials via Raman scattering. X-ray photoelectron spectroscopy studies revealed the distinctive spectral features of the Mn5O8 due to the coexistence of divalent and tetravalent Mn ions. Magnetic measurements confirmed further that Mn5O8 was a mixed valence oxide with an antiferromagnetic transition at about 133 K. The decreased Neel temperature of the Mn5O8 nanorods Suggested the possible presence of the finite size effect, which accounted also for the red-shift of the corresponding Raman bands in comparison with those of the bulk counterparts.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据