期刊
JOURNAL OF PHYSICAL CHEMISTRY C
卷 113, 期 3, 页码 914-924出版社
AMER CHEMICAL SOC
DOI: 10.1021/jp808825c
关键词
-
The synthesis of nanocrystalline solid solutions of general formula CexZr1-xO2 (x = 0.1, 0.25, 0.5, 0.75, and 0.9) using a citrate complexation technique was followed with thermochemical methods, and the resulting powders were characterized using X-ray diffraction (XRD) and electron microscopy (scanning electron microscopy and high-resolution transmission electron microscopy (HRTEM)). Qualitative analysis of XRD data indicated that the samples exhibited either a cubic (Fm3m) or a tetragonal (P4(2)/nmc) phase, depending on CeO2 content. Electron diffraction results were consistent with the XRD findings. In HRTEM, the internal crystal structure of the nanoparticles was observed to be highly ordered and primary particle size data were collected. Average crystallite size, obtained from the XRD data, was 4.8-8.3 nm, with the larger values at the compositional extremes. A similar trend was observed in HRTEM, although values were generally slightly higher. The Ce0.5Zr0.5O2 solid solution had the smallest crystallites (4.8 nm) and the highest specific surface area (45.8 m(2).g(-1)).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据