Dense W, W-1 wt%La2O3 and W-1 wt%Y2O3 samples with fine microstructure were fabricated by microwave sintering method using nano-scaled powders. The FESEM and Tun analysis, thermal conductivity and Vickers micro-hardness measurements were exploited to characterize these samples. It is found that the addition of Y2O3 and La2O3 nano-particles could significantly hinder the grain growth of tungsten in the consolidation process, decreasing the average grain size from 3.21 mu m in pure W down to 0.7 mu m in W-1%Y2O3 sample. The thermal conductivity and relative density of these samples are higher than 120 W/m K and in the range of 95-97%, respectively. The Vickers hardness of W-1%Y2O3 sample reaches as high as 6.91 GPa, 30% higher than that of pure W (5.04 GPa). (C) 2012 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据