JOURNAL OF NON-CRYSTALLINE SOLIDS
卷 364, 期 -, 页码 44-52出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jnoncrysol.2013.01.009
关键词
Compression; Mechanical properties; Pressure history; Borate glass
资金
- Deutsche Forschungsgemeinschaft (DFG) [SPP 1594]
Isostatic pressure-induced changes in elastic constants and micromechanical properties of soda-lime-borate glasses of molar composition xNa(2)O center dot 10CaO center dot(90-x)B2O3 with x = 5,15, and 25 were determined by performing Brillouin scattering and Vickers indentation experiments. An increase of the isostatic pressure up to 570 MPa resulted in an increase of Young's modulus of 19, 11, and 7% and of hardness at 9.81 N load of 33, 22, and 18% for x = 5, 15, and 25, respectively. The decrease in the resistance to crack initiation (ratio of at least 2) and the increase in the crack-to-indent ratio (change>13%) followed the same compositional trend. Consequently, fracture toughness and brittleness of the soda-lime-borate glasses were negatively and positively correlated with isostatic pressure, respectively. These changes were correlated with the overall decrease of the molar volume. (C) 2013 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据