JOURNAL OF NON-CRYSTALLINE SOLIDS
卷 357, 期 1, 页码 170-180出版社
ELSEVIER
DOI: 10.1016/j.jnoncrysol.2010.09.031
关键词
Sodium silicate glasses 5265; XPS X110; Nuclear Magnetic Resonance N220
资金
- National Sciences and Engineering Council of Canada
High resolution Na 1s, O 1s and Si 2p core level XPS spectra of six Na2O-SiO2 glasses ranging in composition from 100 to 45 mol % SiO2 have been collected using the Kratos Ultra Axis instrument with its unique charge compensation system. The O 1s spectra for the glasses are well resolved so that bridging oxygen (BO, Si-O-Si) and non-bridging oxygen (NBO, Na-O-Si) signals can be accurately fitted and quantified without resorting to constraints or assumptions. The same samples were analysed by Si-29 MAS NMR to obtain Q-species abundances from which BO and NBO proportions were calculated. Similar BO:NBO ratios were obtained by both methods over the entire compositional range studied. They are also consistent with most previous XPS and NMR results for glasses containing more than similar to 65 mol % SiO2. Our XPS and NMR experimental results, however, differ somewhat from previously published XPS and NMR results for glasses containing less than about 65 mol % SiO2. Na is mobile in the X-ray beam and mobility causes BO:NBO ratios to increase with time of exposure. Na mobility here has been circumvented to yield reliable BO:NBO ratios of the glasses. The ratios are lower than previously reported in XPS studies and are similar to ratios obtained from our Si-29 MAS NMR results on the same glasses. The XPS and Si-29 MAS NMR results also indicate the presence of a third oxygen species in sodic glasses. As has been proposed for CaSiO3 glass and for sodic and potassic glasses containing La. we suggest that O2- is present in sodic glasses at small concentrations. The O2- content correlates with increased soda content and may be associated with, and instrumental in development of, three dimensional percolation channels in the glasses. The XPS O 1s line width of the BO peak is broader than the NBO peak, indicating more than one contribution to the BO peak. As observed in crystalline Na metasilicate and Na disilicate, BO of Na-silicate glasses may be of two types, one arising from BO bridging two Si atoms, and the second BO signal arising from BO bonded not only to two Si atoms but also to Na. (C) 2010 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据