JOURNAL OF NON-CRYSTALLINE SOLIDS
卷 356, 期 43, 页码 2241-2246出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jnoncrysol.2010.08.005
关键词
Silica; Aerogel; Fly ash; Ambient pressure drying
Silica aerogels were synthesized from the industrial fly ash by ambient pressure drying method The process consists of two stages preparation of sodium silicate solution from fly ash by hydrothermal reaction with sodium hydroxide and synthesis of porous silica aerogels from the obtained sodium silicate solution Silica wet gels were formed by vitriol catalysis or resin-exchange alkali-catalysis of the obtained sodium silicate solution The trimethylchlorosilane(TMCS)/ethanol(EtOH)/hexane mixed solution was used for solvent exchange/surface modification of the wet gel so as to obtain porous silica aerogels via ambient pressure drying The results indicated that the synthesized silica aerogels were lightweight and hydrophobic The BET specific surface area pore volume and average pore diameter were 362 2-907 9 m(2) g(-1) 0 738-4 875 cm(3) g(-1) and 7 69-24 09 nm respectively Particularly the synthesized silica aerogels by resin exchange alkali catalysis method showed uniform mesoporous structure and had much higher specific surface area (907 9 m2 g-1) and pore volume (4 875 cm(3) g(-1)) than that of by vitriol-catalysis process (C) 2010 Published by Elsevier BV
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据