JOURNAL OF NON-CRYSTALLINE SOLIDS
卷 355, 期 52-54, 页码 2588-2595出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jnoncrysol.2009.09.018
关键词
Chemical durability; Corrosion; Fracture; Strength; Scanning electron microscopy; Nanoparticles; Oxide glasses; Defects
资金
- German Research Foundation (DFG) [SFB528]
In alkaline solutions, the reaction of hydroxyl ions with Si-O-Si-groups of the glass network leads to the formation of hydrated surfaces and dissolved silicate. The rate of this corrosion depends on the chemical constitution of the fiber and the alkaline solution as well as on time and temperature. The investigation of the aging of glass and basalt fibers with different chemical constitutions in NaOH and cement solutions shows that the corrosion mechanism changes due to the inhibiting effect of calcium ions. The strength distributions have been evaluated using a Weibull distribution function. The mechanical behavior strongly depends on the chemistry of the solution and determines the parameters of the Weibull distribution function in terms of either single or mixed distributions. The corrosion in NaOH solution leads to a strong dissolution of the outer layer of the glass and basalt fibers, whereas during aging in cement solution at the same pH-value a limited, local attack was revealed. (C) 2009 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据