JOURNAL OF NON-CRYSTALLINE SOLIDS
卷 355, 期 31-33, 页码 1605-1612出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jnoncrysol.2009.06.002
关键词
Glasses; Carbon; Measurement techniques; SEM S100; STEM/TEM; Microscopy; Scanning electron microscopy; TEM/STEM; Microstructure; Porosity; Sol-gel, aerogel and solution chemistry; Aerogels; Surfaces and interfaces; Adsorption; Viscosity and relaxation; Viscosity
资金
- Ministry of the Environment of Japan
Nickel-modified carbon cryogel beads (Ni/CCBs) With uniform particle size were successfully prepared using the syringe injection method, employing sol-gel polycondensation of a resorcinol-formaldehyde (RF) solution containing Ni acetate as a catalyst. This process was followed by solvent exchange, freeze-drying and carbonization in a nitrogen atmosphere. The effect of viscosity. which increased as the sol-gel polycondensation progressed, of the RF solution on both the particle size distributions of the Ni/CCB and the porous Properties was investigated. The influence of Ni content in the initial reactants on the porous properties of the Ni/CCBs was also studied. Monodisperse Ni/CCBs Could be obtained by injection during the initial reaction period, before the steep increase in the viscosity of the RF solution. The porous properties of the Ni/CCBs were independent of the viscosity of the RF Solution. The BET surface area, micropore volume and mesopore volume of Ni/CCBs decreased with increased Ni content, whereas the macropore volume increased with increased Ni content. The size of the Ni nanoparticles dispersed in the carbon matrix of Ni/CCBs was confirmed to range from 30 to 60 nm. (C) 2009 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据