JOURNAL OF NON-CRYSTALLINE SOLIDS
卷 354, 期 18, 页码 2010-2016出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jnoncrysol.2007.11.011
关键词
porosity; sol-gels (xerogels)
Mesoporous MCM-48 silica membranes have been synthesized on porous supports under hydrothermal conditions, using tetraethyl orthosilicate (TEOS) as silica source, cetyltrimethylammonium bromide (CTAB) as template surfactant. And then the templates were removed by solvent extraction instead of calcination. The results of the TG and FT-IR showed that the solvent of 1M HCl/EtOH solution was feasible to extract the templates in the MCM-48 materials and over 90% of the templates were extracted at room temperature for 24 h. The results of XRD, SEM indicated that the MCM-48 membranes were prepared on the porous supports and extraction did not destroy the mesostructure of the MCM-48. The compactness of the extracted MCM-48 membrane was evaluated by the permeation of single gas (N-2 and H-2) with transmembrane pressure of 60-220 kPa. The permeance of N-2 was independent of the transmembrane pressure and the ideal separation factor was about 3.45. All the results demonstrate that the method, solvent extraction to remove surfactant template, is more effective to synthesize high quality MCM-48 membranes than calcination. (c) 2007 Published by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据