期刊
PHYSICA B-CONDENSED MATTER
卷 459, 期 -, 页码 97-104出版社
ELSEVIER
DOI: 10.1016/j.physb.2014.11.091
关键词
Hydrothermal method; Crystallite size; Porosity; Saturation magnetization; Coercivity; Dielectric response
资金
- Department of Science, Technology and Environment, Puducherry, India [DSTE/GIA/RP/JSA1/2008/899]
Nanocrystalline Ni-Zn-Sb ferrites synthesized by hydrothermal method are reported, influence of Sb5+ ions on structural, magnetic and dielectric properties of ferrites is studied. Phase identification, lattice parameter and crystallite size studies are carried out using by X-ray diffraction (XRD). Addition of dopant resulted for decrease in lattice parameter. Crystallite size gets reduced from 62 nm to 38 nm with doping of Antimony. Crystallite size and porosity exhibit similar trends with doping. Morphological study is carried out by Field Emission Scanning Electron Microscopy (FESEM). Strong MR absorption bands at 400-600 cm(-1) confirm the formation of ferrite structure increase of porosity is attributed to the grain size. Doping with Antimony results for decrease in saturation magnetization and increase in coercivity. An initial increase of saturation magnetization for x=0.1 is attributed to the unusually high density. Reversed trend of coercivity with crystallite size are observed. Higher value of dielectric constant epsilon'((omega) is attributed to the formation of excess of Fe2+ ions caused by aliovalent doping of Sb5+ ions. Variation of dielectric constant infers hopping type of conductivity mechanism. The dielectric loss factor tans attains lower values of similar to 10(-2). High ac resistivity rho(omega) of 10(8) Omega cm is witnessed for antimony doped ferrites. Higher saturation magnetization and enhanced dielectric response directs for a possible utility as microwave oscillators and switches. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据