Sb2Se3 nanowires have been prepared by a novel gas induced reduction (GIR) method. The pre-cursor solution prepared by dissolving Sb-2(OCH2CH2O)(3) and SeO2 in a certain solvent was initially separated from the reductant, hydrazine hydrate. The reductant evaporated during the heating process, dissolved into the precursor solution and reacted with Sb3+ and SeO2 and finally Sb2Se3 nanostructures formed. Different solvents including diethanolamine, glycerol, ethylene glycol, deionized water, absolute ethanol and isopropyl alcohol were respectively used for comparison. It was found that when ethylene glycol was used as a solvent, pure, relatively homogeneous, and high aspect-ratio Sb2Se3 nanowires (40 similar to 120 nm in diameter and similar to 100 mu m in length) were prepared. Growth mechanism of the Sb2Se3 nanowires was proposed. The electrochemistry character of the nanowires was investigated via assembling into lithium ion batteries. The discharge capacity of Sb2Se3/Li cell cycled between 0.3 and 2.5 V was performed in the range of 142 similar to 1036 mA.h.g(-1) during the first 30 cycles, with the charge/discharge efficiency increasing from 89.4% to 97.5%.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据