Influence of Structure Parameters and Crystalline Phase on the Photocatalytic Activity of TiO2 Nanotube Arrays

Titanium oxide nanotube arrays (TiO2-NTAs) with different diameters and lengths are prepared by anodization of titanium foils in a water/ethylene glycol solution (5:95 V/V) containing 0.3 wt% NH4F The effects of the diameters, lengths and crystalline phases of the NTAs on the photocatalytic (PC) activity are systematically evaluated. Larger pore diameter results in higher PC activity. The PC activity increases initially and then decreases with lengths for TiO2-NTAs and the optimal length that yields the highest PC activity is observed to be 6.2 mu m. The crystalline phase and corresponding PC activity depend on the calcination temperature and their relationship is also investigated. The amorphous-to-anatase and anatase-to-rutile phase transitions initially occur at 300 and 500 degrees C, respectively. The PC activity of TiO2-NTAs initially increases with calcination temperature from 250 to 500 degrees C and then decreases at higher calcination temperature. The enhanced PC activity observed from the samples annealed at 250-450 degrees C is attributed to the better anatase crystalline structure at higher calcination temperature. The highest PC activity with regard to photodecomposition of methyl orange is observed from TiO2-NTAs calcined at 500 degrees C, which coincides with the anatse-to-rutile phase transformation. The synergistic effect of the anatase TiO2-NTAs and rutile barrier layers facilitate interfacial electron transfer consequently enhancing the PC activity. Further elevation of the calcination temperatures to 550 and 600 degrees C exhibits diminished PC activity because the NTs become shorter due to conversion of the bottom of anatase NTs into rutile film.