期刊
JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY
卷 11, 期 7, 页码 6136-6140出版社
AMER SCIENTIFIC PUBLISHERS
DOI: 10.1166/jnn.2011.4513
关键词
Pt/Al2O3; Dendrimers Encapsulated Nanoparticles; SCR of NOx
Pt/Al2O3 and Pt-Mg/Al2O3 nano composites were successfully prepared by dendrimer templated synthesis route. The obtained dendritic nanoparticles were dispersed in alumina support and they were evaluated for SCR of NOx using methane as reductant. Thermal analysis results of uncalcined samples revealed that the oxygen can accelerate the rate of dendrimer shell decomposition. X-ray diffractograms of 500 degrees C calcined samples disclosed the amorphous nature of materials, whereas 1000 degrees C air calcined samples showed enhanced crystallinity as well as diffraction pattern corresponding to Pt and PtO. HRTEM images of Pt-40-G4OH dendritic nanoparticles showed uniform particulate distribution with average particle size of 2.4 nm. The STEM results of 0.5 Pt/Al2O3 sample calcined at 500 degrees C exhibited a wide range of particles between 2 and 20 nm. This indicates the huge segregation of platinum metal particles during impregnation and subsequent calcination. Among the synthesized materials 0.5 wt% Pt/Al2O3 sample showed excellent conversion and selectivity for SCR of NOx.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据