JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY
卷 11, 期 3, 页码 2413-2420出版社
AMER SCIENTIFIC PUBLISHERS
DOI: 10.1166/jnn.2011.3524
关键词
Nano-Hematite; Chemical Synthesis; Optical Properties; Ultraviolet Radiation; In Vitro SPF/PF-UVA Tests
Hematite nanoparticles were synthesized for ultraviolet filtration application by the precipitation method followed by calcination at different temperatures. A range of crystallite sizes between 37 and 85 nm (as determined by the Scherrer formula) was obtained, according to the temperature used for the calcination. An increase in the absorbance with increasing crystallite size was observed over the whole ultraviolet B and A range. The experimental band gap was 2.94 eV for the sample calcined at 500 degrees C and 3.08 eV for the sample calcined at 300 degrees C. The in vitro sun protection factor and protection factor-ultraviolet A of a water-in-oil emulsion made with the sample calcined at 500 degrees C as active ingredient were 9.21 and 8.81, respectively, which is higher than the protection factor-ultraviolet A values obtained for titanium dioxide and zinc oxide at the same mass concentration. The emulsion was found to be photostable.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据