DOI: 10.1166/jnn.2009.1259
关键词
Photoluminescence; MgAl2O4 Spinel; Eu3+ and Eu2+; Nanocrystallites; Afterglow
In the present work, a modified Pechini method was employed to prepare nanostructured MgAl2O4 spinel powders doped with Eu3+ ions. The XRD analyses demonstrated that the powders were single-phase spinel nanopowders with high crystallite dispersion. The average spinel particle size was determined to be approximate to 15 nm for calcination at 700 degrees C, and approximate to 20 at 1000 degrees C. The emission and excitation spectra measured for the samples calcinated at 700 and 1000 degrees C demonstrated characteristic spectra of Eu3+ ions as well as were measured the emission spectra of Eu2+ ions for the samples calcinated at 700 degrees C. The effect of MgAl2O4 grain sizes on luminescence properties was noticed. To explain these differences a detailed analysis of luminescence spectra by the Judd-Ofelt theory has been performed.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据