JOURNAL OF NANOPARTICLE RESEARCH
卷 13, 期 1, 页码 127-138出版社
SPRINGER
DOI: 10.1007/s11051-010-0010-7
关键词
Copper; Nanoparticles; Colloid; Polyol synthesis; Microwave
Microwave heating was applied to synthesize copper colloidal nanoparticles by a polyol method that exploits the chelating and reducing power of a polidentate alcohol (diethylenglycol). The synthesis was carried out in the presence of eco-friendly additives such as ascorbic acid (reducing agent) and polyvinylpirrolidone (chelating polymer) to improve the reduction kinetics and sols stability. Prepared suspensions, obtained with very high reaction yield, were stable for months in spite of the high metal concentration. In order to optimize suspensions, synthesis parameters were modified and the effects on particle size, optical properties, and reaction yield were investigated. XRD analysis, scanning transmission electron microscopy (STEM), and DLS measurements confirmed that prepared sols consist of crystalline metallic copper with a diameter ranging from 45 to 130 nm. Surface plasmon resonance (SPR) of Cu nanoparticles was monitored by UV-Vis spectroscopy and showed both a red shift and a band weakening due to nanoparticle diameter increase. Microwave use provides rapid, uniform heating of reagents and solvent, while accelerating the reduction of metal precursors and the nucleation of metal clusters, resulting in monodispersed nanostructures. The proposed microwave-assisted synthesis, also usable in large-scale continuous production, makes process intensification possible.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据