JOURNAL OF MOLECULAR STRUCTURE
卷 1033, 期 -, 页码 200-207出版社
ELSEVIER
DOI: 10.1016/j.molstruc.2012.08.040
关键词
Melt-quenching; Optical absorption; Photo luminescence; FTIR; Bismuth borate glasses
资金
- University Grants Commission, New Delhi, Government of India [F.4-1/2006(XI Plan/BSR)]
Transparent BaBiBO4:CoO glasses of composition 10BaO center dot 20Bi(2)O(3)center dot(70 - x)B2O3-xCoO (wt%) where 0 <= x <= 2.0, were synthesized and characterized by XRD. Physical properties coupled with Spectroscopic (optical absorption, photoluminescence and FTIR spectra) and dielectric studies were carried out. The area under the absorption band corresponds to (4)A(2)(F-4) -> T-4(1)(F-4) transition of Co2+(IV) is gradually increased up to 1.5 wt% of CoO and then it is decreased at 2.0 wt% of CoO. It is also supported by decrease in Co2+ ion concentration N-i at 2.0 wt% of CoO calculated from density values. The concentration of luminescence centers of bismuth ions [Bi2+ ions in the visible region] decreased up to 1.5 wt% of CoO and increased beyond this concentration. Further, it is also noted that at higher concentrations of dopant Co2+ ions acts as redox partner of Bi3+ and reduce it to Bi2+ state. The optical band gap energy (E-g) is found to increase than the pure with 0.5 wt% of CoO and beyond this concentration the E-g value is gradually decreased. It is due to the formation of covalent Co-O-B bonds in the glass network with tetrahedral CoO4 units. From FTIR studies, at higher concentrations due to gradual increase in CoO6 units leads to formation of BO3 and BiO6 units along with NBOs. The above results are also supported by observed decrease in dielectric constant epsilon', loss tan delta and sigma(ac) with the initial introduction 0.5 wt% of CoO in the glass matrix at any frequency and temperature except in the relaxation temperature region. (C) 2012 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据