The superbasic ZrO2 (ZrO2-KOH) with high surface area was prepared by reflux-digestion of ZrO(OH)(2) gel in mother liquor and examined as a support promoting ammonia synthesis by particulate Ru. The TEM image of Ru/ZrO2-KOH catalyst indicates that the size of Ru particles is in the range of 1.5-3.2 nm, which is the optimum size of Ru particles for the maximum number of B-5-type sites. Additionally, the characterizations including CO2-TPD, XPS and N-2-TPD demonstrate that the Ru particles supported on ZrO2-KOH exhibit higher electron density compared to that of Ru/ZrO2 catalyst. As a result, the dissociative adsorption of N-2 over Ru/ZrO2-KOH is more facile than that over Ru/ZrO2 catalyst. Thus, the Ru/ZrO2-KOH catalyst shows an excellent activity for ammonia synthesis especially under the conditions of low temperature and pressure. The highest reaction rate of Ru/ZrO2-KOH is 16.91 mmol/(g h) at 698 K and 3.0 MPa, which is much higher than that of various Ru catalysts supported on other supports. Crown Copyright (c) 2013 Published by Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据