JOURNAL OF MICROSCOPY-OXFORD
卷 233, 期 3, 页码 432-441出版社
WILEY-BLACKWELL PUBLISHING, INC
DOI: 10.1111/j.1365-2818.2009.03131.x
关键词
Dynamic grain growth; EBSD; in situ; particle coarsening
类别
The effect of hot deformation on fully recrystallized aluminium-copper alloys (Al-4wt%Cu and Al-33wt%Cu) with different volume fractions of CuAl(2) has been studied. The alloys are Zener pinned systems with different superplastic properties. Strain-induced grain growth, observed in both alloys, was quantitatively estimated by means of electron microscopy and EBSD and compared with the rate of static grain growth. Surface marker observations and in situ hot-deformation experiments combined with EBSD were aimed at clarifying the mechanisms responsible for the changes in the deformed microstructures. A sequence of secondary and backscattered electron images and EBSD maps was obtained during in situ SEM deformation with different testing conditions. Overlaying EBSD maps for the Al-4wt%Cu with channelling contrast images showed that grain boundary motion occurred during deformation, creating a layered structure and leading to an increase in size of some grains and shrinkage of others. Of a particular interest are results related to behaviour of CuAl(2) in superplastic Al-33wt%Cu during deformation, including several problems with the use of EBSD in this alloy.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据