期刊
JOURNAL OF MEMBRANE SCIENCE
卷 450, 期 -, 页码 215-223出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.memsci.2013.09.012
关键词
Gas separation membrane; Zeolitic-imidazolate framework; ZIF-8; Propylene/propane separation; Counter diffusion
资金
- JSPS KAKENHI [25820385]
- Cooperative Research Program of Network Joint Research Center for Materials and Devices
- Grants-in-Aid for Scientific Research [25820385] Funding Source: KAKEN
The contribution of diffusive separation of propylene/propane was determined from the permeation properties of zeolitic-imidazolate framework-8 (ZIF-8)(1) membranes. These membranes were prepared using a counter diffusion method, resulting in the formation of an 80 mu m thick ZIF-8 layer on the outermost section of a porous so alumina capillary substrate. Single component gas permeation properties were investigated using helium, hydrogen, carbon dioxide, oxygen, nitrogen, methane, propylene, and propane at temperatures ranging from 298 to 363 K. The molecular sieve gas permeation properties of the ZIF-8 membranes increased with reaction time, which is consistent with the evolution of ZIF-8 crystal formation. The ZIF-8 membrane permeances of hydrogen and propylene reached 9.1 x 10(-8) and 2.5 x 10 (9) mol m (2) Pa (1), respectively. The ideal separation factors for hydrogen/propane and propylene/propane at 298 K were found to be 2000 and 59, respectively. The diffusion separation factor increased with decreasing temperature, reaching 23, while the solution separation factor remained 2.7. Therefore, the separation of propylene/propane was attributed to be mainly governed by diffusive separation. (C) 2013 Published by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据