期刊
JOURNAL OF MEMBRANE SCIENCE
卷 428, 期 -, 页码 78-85出版社
ELSEVIER
DOI: 10.1016/j.memsci.2012.11.005
关键词
SrCo0.8Fe0.1Ga0.1O3-delta (SCFG); Oxygen permeation membrane; Perovskite; Hollow fiber membrane
资金
- National University of Singapore
- A*STAR [092-138-0022, 279-000-292-305]
- NEA [1002114, 279-000-333-490]
- National Science Foundation of China [210761118]
A new SrCo0.8Fe0.1Ga0.1O3-delta (SCFG) perovskite material has been successfully synthesized using an EDTA-CA complexing method. The resultant SCFG powder calcined at 900 degrees C shows perovskite-type crystal structure upon calcination at 900 degrees C for 5 h. The oxygen-permeating SCFG hollow fiber membrane prepared from the SCFG powder by the phase inversion-sintering method shows a unique asymmetric structure with porous internal-external surfaces and a dense middle layer. This SCFG hollow fiber membrane is able to achieve a good oxygen permeability of 3.5 mL min(-1) cm(-2) at 950 degrees C and 0.55 mL min(-1) cm(-2) at 600 degrees C when supplied with air using He as a sweep gas. The presence of Ga was found to significantly lower the activation energy of SCFG hollow fiber membrane. The unique asymmetric structure played a critical role in elevating the critical temperature to 900 degrees C for transition from surface-reaction to bulk-diffusion controlled regime. Furthermore the SCFG hollow fiber membrane is very stable under reducing environment of 20 mL min(-1) methane for at least 100 h with an enhanced permeation of 3.4 mL min(-1) cm(-2) at 900 degrees C. (C) 2012 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据