期刊
JOURNAL OF MEMBRANE SCIENCE
卷 415, 期 -, 页码 745-757出版社
ELSEVIER
DOI: 10.1016/j.memsci.2012.05.066
关键词
Nanohybrid multilayer membrane; Pervaporation; Dynamic layer-by-layer assembly; Hollow fiber; Acetone-water mixture
资金
- Natural Science Foundation of Beijing [8122010]
- National Basic Research Program of China [2009CB623404]
- National Natural Science Foundation of China [21176007]
- Program for Innovative Research Team in Beijing Academy of Science and Technology [IG201204N]
In this article, an organic-inorganic nanohybrid multilayer membranes have been developed by incorporating zirconium dioxide (ZrO2) and alumina oxide (Al2O3) nanoparticles into polyelectrolyte complexes such as poly(diallyldimethyl ammonium chloride)/poly(sodium styrene sulfonate) and poly(ethyleneimine)/polyacrylic acid. These nanohybrid multilayers were successfully formed on to both flat sheets and hollow fiber polyacrylonitrile ultrafiltration support membranes by layer-by-layer (LbL) assembly of polycation- and polyanion-coated nanoparticles and used for pervaporation dehydration of an acetone-water mixture. We show that the matching between the size of the NPs and the supporting membrane pore size strongly influences the morphologies and performance of the multilayer membranes. SEM-EDX and AFM analyses suggest that the ZrO2 NPs are mostly distributed on the substrate surface while the Al2O3 NPs are able to migrate into the substrate membrane pores. This is due to the differences between the sizes of the two NPs and results in an increase of the surface roughness of the ZrO2 nanohybrid multilayer membrane while that oft he Al2O3 nanohybrid multilayer membrane decreased. The ZrO2 nanohybrid multilayer membrane was able to overcome the trade-off phenomenon, which enabled both higher flux and larger separation factor. However, for the Al2O3 nanohybrid multilayer membrane, the separation factor increased while the corresponding flux values were somewhat lower than those observed for pristine polymeric membranes. (c) 2012 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据