Gas separation; Natural gas; Carbon dioxide; Hollow fiber; Polyimide; Toluene
资金
- Chevron Energy Technology Company
- King Abdullah University of Science and Technology (KAUST) [KUS-I1-011-21]
The performance of defect-free cross-linkable polyimide asymmetric hollow fiber membranes was characterized using an aggressive feed stream containing up to 1000 ppm toluene. The membrane was shown to be stable against toluene-induced plasticization compared with analogs made from Matrimid (R), a commercial polyimide. Permeation and sorption analysis suggest that the introduction of toluene vapors in the feed subjects the membrane to antiplasticization, as the permeance decreases significantly (to less than 30%) under the most aggressive conditions tested. Separation efficiencies reflected by permselectivities were less affected. The effect of the toluene on the membrane was shown to be reversible when the toluene was removed. (C) 2010 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据