1,3,5-Tris(4-aminophenoxy) benzene (TAPOB) and 2,2-bis [4-(3,4-dicarboxyphenoxy) phenyl] propane dianhydride (BPADA) were used to synthesize an amino-terminated hyperbranched polyimide (AM-HBPI). Then, the 2-methacryloyloxyethyl phosphorylcholine-modified hyperbranched polyimide (HBPI-MPC) was obtained through the graft modification of MPC onto AM-HBPI by Michael addition. The infrared spectroscopy and X-ray photoelectron spectroscopy spectra showed MPC molecules were successfully grafted onto the HBPI molecules. The HBPI-MPC films exhibited slightly decreased thermal stabilities with 5% weight loss temperature in the range of of 418-483 degrees C in nitrogen, compared with the pure HBPI film. With the increase of MPC grafting amount, the static water contact angles decreased from average 84.0 degrees of the pure HBPI film to average 45.0 degrees of the HBPI-MPC film with 20% MPC. Meanwhile, the increased surface roughness of the HBPI-MPC films increased the contact areas with the platelets, enhancing their anticoagulant efficiency. The number of platelet adhesion declined and the shape of platelet changed from flat to round. The recalcification times grew from average 300 s of pure HBPI to average 551 s of the HBPI-MPC film with 20% MPC, indicating improved anticoagulant properties and biocompatibility. Bacterial adhesion test also demonstrated the number of bacterial adhesion was significantly reduced and antibacterial properties were improved. Thus, the HBPI-MPC films have great application prospects as biomedical anticoagulant materials.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据