The effect of nano-sized WO3 (40 nm) addition on the physical and magnetic properties of Bi-2212 superconductors was investigated by X-rays diffraction (XRD), scanning electron microscopy, dc electrical resistivity, magnetic hysteresis loop measurements and Vickers microhardness measurements. XRD observations indicated that the number and type of nonsuperconductor phases changes with increasing nano-sized WO3 content. With increase in W content the critical temperature decreases and the resistivity value at room temperature for sample W4 significantly increases. In addition, the adding of W into the samples causes a remarkable decrease of the area enclosed hysteresis cycles. The critical current density (J(c)) at 10 K of the all W-doped samples was lower than that of the pure sample, indicating that superconductor properties of samples negatively affect when nono-sized W particles enters into the structure. In addition, the obtained microhardness values in this work indicated that the all samples have the typical indentation size effect behavior.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据