Rapid microwave synthesis of δ-MnO2 microspheres and their electrochemical property

期刊

出版社

SPRINGER
DOI: 10.1007/s10854-013-1078-5

关键词

-

资金

  1. National Natural Science Foundation of China [20471022, 40673051, 21271082]

向作者/读者索取更多资源

The delta-MnO2 microspheres as well as the delta-MnO2 microspheres/ delta-MnO2 nanorods mixture were synthesized by reduction of KMnO4 under microwave irradiation. The morphology and structure of the as-prepared products were characterized by powder X-ray diffraction (PXRD), field-emission scanning electron microscopy (FE-SEM), energy-dispersive X-ray spectroscopy (EDX), Brunauer-Emmett-Teller (BET) measurements and Raman spectra. Electrochemical performances of the samples were examined using cyclic voltammetry (CV) and galvanostatical discharge-charge test in Na2SO4 and Li2SO4 aqueous electrolyte, respectively. It was found that the nearly ideal rectangular shapes of the CV curves show that these samples exhibited good pseudo-capacitor properties in the voltage range from 0.0 to 1.0 V. The test of long-term cycling stability indicated that two samples all have a reasonably good stability. However, the delta-MnO2 microspheres possessed a lower specific surface area while a higher supercapacitance than those of the delta-MnO2 micropheres/alpha-MnO2 nanorods mixture did. The presence a few fraction delta-MnO2 impurities reduces the specific capacitance of delta-MnO2 electrode. Because of the crystal structure and morphologies are two such important parameters that have to be taken into account in this work.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.6
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据