JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
卷 26, 期 12, 页码 1139-1142出版社
JOURNAL MATER SCI TECHNOL
DOI: 10.1016/S1005-0302(11)60014-5
关键词
Carbon/carbon composites; Oxidation; Coating
资金
- National Natural Science Foundation of China [50902111, 90716024]
- China Postdoctoral Science Foundation [20080441186]
- China Postdoctoral Science Special Foundation [200902603]
A C/SiC/Si-SiC multilayer coating for protecting carbon/carbon (C/C) composites against oxidation was prepared by slurry and pack cementation. X-ray diffraction (XRD) and energy dispersive spectroscopy (EDS) analysis showed that the inner coating obtained from the slurry and pack cementation was a C/SiC gradient layer acting as bonding layer, and the exterior coating formed in the second pack cementation was a Si-SiC double phase coating. Oxidation tests at 1873 K in air showed that the coating exhibited excellent oxidation protective ability and thermal shock resistance. The coating could effectively protect C/C composites from oxidation at 1873 K in air for 170 h and undergo the thermal cycling between 1873 K and room temperature for 8 cycles. The weight loss of the coated C/C composites is due to the formation of cracks and holes in the coating and the volatilization of SiO2 glass at high temperature.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据