Cubic garnet of nominal composition Li7La3Zr2O12 (LLZO) is of interest as a possible electrolyte in a Li-metal halide battery composed of molten Li and an insoluble metal halide as electrodes operating in the temperature range of similar to 300-350 A degrees C. As a consequence, the chemical stability of LLZO with molten Li in this temperature range was investigated. After heating in molten Li, the LLZO surface had undergone chemical coloration. X-diffraction, X-ray photoemission spectroscopy, electron paramagnetic resonance, and heat-treatment experiments suggest that chemical coloration is a result of the formation of color centers, composed of an electron trapped at an oxygen vacancy. It was also observed that after immersion in molten Li that LLZO exhibited intergranular cracking. It is believed that cracking results from stresses generated from an increased Li+ content, gained during immersion.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据