JOURNAL OF MATERIALS SCIENCE
卷 47, 期 6, 页码 2548-2558出版社
SPRINGER
DOI: 10.1007/s10853-011-6078-3
关键词
-
资金
- National Natural Science Foundation of China [50873073, 20974076]
- Priority Academic Program Development of Jiangsu Higher Education Institutions
- Major Program of Natural Science Fundamental Research Project of Jiangsu Colleges and Universities [11KJA43001]
- Qing Lan Project of Jiangsu Province in China
- Suzhou Applied Basic Research Program [SYG201141]
A novel kind of incompletely condensed polyhedral oligomeric silsesquioxane (TAP-POSS) containing allyl groups was successfully synthesized, and its structure was characterized by fourier transform infrared, nuclear magnetic resonance (H-1-NMR and Si-29-NMR) and X-ray diffraction. In addition, TAP-POSS was hybridized with 2,2'-diallylbisphenol A (DBA)-modified 4,4'-bismaleimidodiphenylmethane (BDM) resin to develop a new kind of hybrids with simultaneously improved thermal stability and dielectric properties. Compared with BDM/DBA resin, the BDM/DBA/TAP-POSS hybrids have obviously increased thermal resistance reflected by the increased glass transition temperature (T (g)) and char yield at high temperature. For example, the T (g) of modified BDM/DBA resin with only 3.0 wt% TAP-POSS is 330 A degrees C, which is 36 A degrees C higher than that of pure BDM/DBA resin. On the other hand, the dielectric properties over wide frequency and temperature ranges are thoroughly investigated, and results show that the dielectric constant and loss of all hybrids are not only lower than those of BDM/DBA resin over the whole frequency and temperature ranges tested, but also exhibit smaller dependence on temperature and frequency. These phenomena can be explained from the variety of cross-linked structure induced by the presence of TAP-POSS. The outstanding integrated properties of BDM/DBA/TAP-POSS hybrids suggest that TAP-POSS has advantages over conventional POSS, thus the method proposed herein is a new approach to develop high performance structural/functional materials for cutting-edge industries.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据