Particle size-dependent electrical properties of nanocrystalline NiO

Nickel oxide nanoparticles are formed by chemical precipitation and subsequent drying and calcinations at temperatures a parts per thousand yen523 K. Samples are characterized using X-ray diffraction and BET surface area measurements indicating the formation of a single NiO phase whose crystallite size increases with increasing calcination temperature. The electrical properties are examined by measuring DC and AC conductivities and dielectric properties as functions of temperature. Electrical conductivities first slightly increases with increasing particle size up to 7-10 nm and are about 8 orders of magnitude higher than that of NiO single crystals. Further increasing the particle size above 10 nm, leads to a monotonic decrease of conductivity. The data are discussed in view of variations of grain boundary as well as triple junction volume fractions as the particle size varies. At temperatures above theta(D)/2 (theta(D) is the Debye temperature), the conductivity is ascribed to a band-like conduction due to the large polaron. The activation energy of conduction was found to be minimal for the highly conducting samples of 7-10 nm, and gradually increases to similar to 0.5 eV with increasing the particle size above 10 nm. For T < theta(D)/2, the conductivity is best described by variable-range-hopping models. Model parameters are thus estimated and presented as functions of particle size. Frequency as well as temperature dependencies of the AC conductivity and dielectric constant exhibit trends usually observed in carrier dominated dielectrics.