JOURNAL OF MATERIALS PROCESSING TECHNOLOGY
卷 213, 期 11, 页码 1818-1824出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jmatprotec.2013.04.018
关键词
Friction stir welding; Embedded rod; Tensile strength
资金
- National Science Council in Taiwan [NSC-100-2221-E-110-038]
A pinless tool design was proposed to achieve high butt tensile strength in aluminum alloy sheets (similar to 3 mm thick) in friction stir welding (FSW), where a 7 mm long cylindrical insert rod made of aluminum alloy was tightly embedded into a hollow cylindrical tool. The effects of rod diameter (d) on the welding properties and mechanism of weld formation were investigated. For friction stir spot welding (FSSW), the maximum rate of temperature rise was about 12.8 degrees C/s, and the failure load was about 2 kN for this pinless tool (d = 10 mm), with these being about 7.4 degrees C/s and 1.35 kN for the plain one. For FSW, the failure load was about 1.46 kN for this tool, and about 0.72 kN for the plain one. The abutting edges of sheets with a thickness of 3 mm could be welded using this pinless tool. (C) 2013 Published by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据