JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
卷 20, 期 9, 页码 1569-1574出版社
SPRINGER
DOI: 10.1007/s11665-011-9843-1
关键词
aging; Al-4Zn-2Mg alloy; cryorolling; secondary precipitation; tensile behavior; ultrafine-grain structure
资金
- National Metallurgical Laboratory, Jamshedpur, India
An Al-4Zn-2Mg alloy was subjected to cryorolling (CR) followed by short annealing. An average grain size of similar to 100 nm was achieved. Cryorolled samples showed large reduction in grain size due to suppression of dynamic recovery and absence of annihilation of dislocations, as compared to room temperature rolled samples. Further, the ultrafine-grained (UFG) Al-4Zn-2Mg alloy when subjected to natural aging showed an improved strength of similar to 413 MPa with ductility of similar to 25%, as compared to similar to 360 MPa and 22% ductility in peak aged condition of coarse-grained alloy. However, UFG alloy in peak aging condition, exhibited a relatively strength (similar to 375 MPa) and 24% ductility combinations than the natural aging condition. The latter is attributed to dynamic precipitation and stored energy. In the present study, it is demonstrated that simultaneous improvement in strength as well as ductility can be achieved for the Al-4Zn-2Mg alloy through CR and controlled heat treatment combinations.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据