期刊
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
卷 20, 期 9, 页码 1563-1568出版社
SPRINGER
DOI: 10.1007/s11665-011-9840-4
关键词
alumina ceramic; bonding mechanism; brazing; mechanical property; metallization
资金
- National Natural Science Foundation of China [51002114, 10825210]
- National Basic Research Program of China [2011CB610305]
- National 111 Project of China [B06024]
- 13115'' project of Shaanxi Province [S2010ZDKG704]
- Postdoctoral Science Foundation of China [20100470089]
Al(2)O(3) ceramic/stainless steel joints were fabricated by activated molybdenum-manganese (Mo-Mn) sintering metallization plus vacuum brazing using Ag-28 wt.% Cu alloy. The bonding mechanisms including metallization and interfacial bonding were analyzed and discussed by means of scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and x-ray diffraction (XRD). Tests were also carried out to examine the influence of brazing on joint shear strength. The metallization mechanisms of glassy phase migration and chemical reaction were confirmed experimentally, while Ni coating was found to play a key role in the joining of metallized ceramic to metal via the Ag-Cu filler layer. As a result of the joining, the average shear strength of the joints exceeds 95 MPa, with the maximum reaching 110 MPa.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据