Properties of Porous TiNbZr Shape Memory Alloy Fabricated by Mechanical Alloying and Hot Isostatic Pressing

In the past decades, systematic researches have been focused on studying Ti-Nb-based SMAs by adding ternary elements, such as Mo, Sn, Zr, etc. However, only arc melting or induction melting methods, with subsequent hot or cold rolling, were used to fabricate these Ni-free SMAs. There is no work related to powder metallurgy and porous structures. This study focuses on the fabrication and characterization of porous Ti-22Nb-6Zr (at.%) shape memory alloys produced using elemental powders by means of mechanical alloying and hot isostatic pressing. It is found that the porous Ti-22Nb-6Zr alloys prepared by the HIP process exhibit a homogenous pore distribution with spherical pores, while the pores have irregular shape in the specimen prepared by conventional sintering. X-ray diffraction analysis showed that the solid solution-treated Ti-22Nb-6Zr alloy consists of both beta phase and alpha aEuro(3) martensite phase. Morphologies of martensite were observed. Finally, the porous Ti-22Nb-6Zr SMAs produced by both MA and HIP exhibit good mechanical properties, such as superior superelasticity, with maximum recoverable strain of similar to 3% and high compressive strength.