JOURNAL OF MATERIALS CHEMISTRY
卷 22, 期 1, 页码 109-114出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c1jm13213j
关键词
-
资金
- National High Technology Research and Development Program of China [2008AA032102]
- NSF of China [50573014, 50773012]
- Shanghai Nanotechnology Program [1052nm00400]
A synergistic self-organization method was proposed to prepare multifunctional superhydrophobic composite films, which combined well-exfoliated graphene nanosheets (GNs) with a conjugate polymer (poly(3-hexyl thiophene), P3HT) through a simple solution-deposition process. The composite film can be rapidly prepared on various substrates; typically only a few minutes were necessary when the P3HT-GN suspension was coated on a metal mesh. The 35 wt% P3HT composite film is superhydrophobic with a contact angle of 159.2 degrees, an electrical conductivity up to 6560 S m(-1) and specific electromagnetic interference shielding effectiveness (43.7 dB cm(3) g(-1)) four times greater than solid copper. It has a porous structure with the bulk density of 0.76 g cm(-3), separation efficiency of over 98% for the noctane/water mixtures in volume ratios of 1 : 1-1 : 15, and good environmental stability with a capacity to endure thermal treatment at 200 degrees C and organic solvents such as methanol, acetone and DMF etc. This synergistic self-organization method was also applied to prepare superhydrophobic P3HT-montmorillonite (MMT) composite films with a contact angle of 161 degrees and a high adhesion capacity to water droplets, proving a versatile method in fabricating functional superhydrophobic films suited to practical applications.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据