期刊
JOURNAL OF MATERIALS CHEMISTRY
卷 22, 期 43, 页码 23049-23056出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c2jm32989a
关键词
-
资金
- National Research Foundation [NRF2009EWT-CERP001-036]
Hollow-structured alpha-Fe2O3 nanofibers were successfully synthesized by a simple electrospinning technique using iron acetylacetonate (Fe(acac(3))) and polyvinylpyrrolidone (PVP) precursor. Fe (acac)(3)-PVP composite fibers were calcined at high temperature to form an interconnected ID hollow-structure of alpha-Fe2O3 nanofibers. Thermogravimetric analysis (TGA), X-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM) and Brunauer-Emmett-Teller (BET) were employed to characterize alpha-Fe2O3 a hollow fibers. Based on the characterization results, a formation mechanism for electrospun alpha-Fe2O3 hollow fibers is proposed. Electrochemical measurements showed that the hollow-structure of alpha-Fe2O3 nanofibers played an important role in improving the electrode cycle stability and rate capability in lithium ion batteries. The alpha-Fe2O3 hollow fiber anodes exhibit a high reversible capacity of 1293 mA h g(-1) at a current density of 60 mA g(-1) (0.06 C) with excellent cycle stability and rate capability. Based on our study this high performance is attributed to the interconnected hollow-structure of large aspect ratio alpha-Fe2O3 cc nanofibers, which makes them a potential candidate for lithium ion batteries.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据