We herein present results obtained from our study of flat and uniform polymer-blended small-molecular semiconductor thin films. These films were produced for organic thin film transistors (OTFTs), using a simple pre-metered horizontal dipping process. The organic semiconductor thin films were composed of a small molecular 6,13-bis(triisopropylsilylethynyl)-pentacene (TIPS-PEN) composite blended with a polymer binder of poly(alpha-methylstyrene) (PaMS). We show that the premetered solution-coating process allowed the critical control of the thickness of the TIPS-PEN: PaMS film; extremely thin films could be produced using the downstream meniscus of the solution at high speeds (of the order of a few metres per minute). The fabricated TIPS-PEN: PaMS OTFTs exhibited a maximum field-effect mobility of 0.22 cm(2) V-1 s(-1), and on/off ratios of over 10(5), that were consistently superior to those of conventional spin-cast devices. These results demonstrate that horizontal dipcoated TIPS-PEN: PaMS films show considerable promise for the production of reliable, reproducible, high-performance OTFTs.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据