JOURNAL OF MATERIALS CHEMISTRY
卷 21, 期 11, 页码 3740-3744出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c0jm03573d
关键词
-
资金
- ITRI [9301XS1J31]
- NSC [97-2113-M-002-012-MY3, 97-3114-M-002-002]
- Economic Affair [97-EC-17-A-07-S1-043]
A highly intense green-emitting phosphor BaY2Si2Al2O2N5 : Eu2+ (BYN : Eu2+) peaking at 511 nm was synthesized by a solid state reaction. The structure refinement, luminescence properties of BYN : Eu2+ phosphors as well as their thermal quenching and the fabrication of white-light-emitting diodes (W-LEDs) were firstly investigated. By partially substituting Ba by Sr, namely (Ba, Sr)Y2Si2Al2O2N5 : Eu2+ (BSYN : Eu2+), the emission peak was shifted to 565 nm, giving a yellow-orange color, due to the splitting of the 5d energy level. By utilizing a mixture of blue-emitting BaMgAl10O17 : Eu2+, green-emitting BYN : Eu2+ and red-emitting CaAlSiN3 : Eu2+ phosphors as light converters, an intense white GaN-based n-UV-LED (380 nm) was fabricated to a exhibit good color-rendering index R-a of 84.5 at a correlated color temperature of 5089 K and CIE coordinates of (0.3425, 0.3478). Based on these results, we are currently evaluating the potential application of BYN : Eu2+ as a green-emitting near-UV convertible phosphor.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据