JOURNAL OF MATERIALS CHEMISTRY
卷 21, 期 34, 页码 12880-12888出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c1jm11850a
关键词
-
资金
- National Science Council, Taiwan, Republic of China [NSC-100-ET-E-007-001-ET]
We herein describe our use of a water-ethylene method to prepare a composite material consisting of platinum nanoparticles and graphene. Results obtained using XPS and XRD show that the degree of reduction of graphene was increased by the incorporation of Pt, and in addition, the increased concentration of defects was confirmed by the D/G ratio of the Raman spectra obtained. In comparison with Pt films, results obtained using CV and EIS showed that the electrocatalytic ability of the composite material was greater, and afforded a higher charge transfer rate, an improved exchange current density, and a decreased internal resistance. SEM images showed that the morphology of PtNP/GR counter electrodes is characterized by a smooth surface, however, resulting in a lower resistance to diffusion, thereby improving the total redox reaction rate that occurs at the counter electrode. PtNP/GR electrodes have a number of advantages over other electrodes that consist solely of graphene or Pt films, including a high rate of charge transfer, a low internal resistance, and a low resistance to diffusion. In our study, we showed that DSSCs that incorporate platinum-grafted graphene had a conversion efficiency of 6.35%, which is 20% higher than that of devices with platinized FTO.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据