Nickel sulfide nanoparticles were synthesized by thermal decomposition of nickel acetylacetonate in a mixed solution of 1-dodecanethiol and a high-boiling solvent. The crystal phase and morphology of the obtained samples by changing the reaction time, reaction temperature, and the kind of the solvents were characterized by X-ray diffraction measurements and transmission electron microscopy. By using oleylamine as a coordinating solvent, Ni9S8 nanorods with the size of about 100 nm were obtained at 280 degrees C for 5 hours. On the other hand, NiS nanoparticles with the size of about 50 nm were obtained by using 1-octadecene as a noncoordinating solvent. Nickel sulfide crystals with different phase and morphology were obtained by selecting the solvent. The all-solid-state cells using NiS nanoparticles with the size of about 50 nm as active materials were fabricated. The 80Li(2)S center dot 20P(2)S(5) (mol%) glass-ceramic was used as a solid electrolyte. The cell Li-In/NiS exhibited the initial discharge capacity of 780 mA h g(-1) at 0.13 mA cm(-2) and the good cycle performance during 20 cycles.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据